The field induced e31,f piezoelectric and Rayleigh response in barium strontium titanate thin films
Abstract
The electric field induced e31,f piezoelectric response and tunability of Ba0.7Sr0.3TiO3 (70:30) and Ba0.6Sr0.4TiO3 (60:40) thin films on MgO and silicon was measured. The relative dielectric tunabilities for the 70:30 and 60:40 compositions on MgO were 83% and 70%, respectively, with a dielectric loss of less than 0.011 and 0.004 at 100 kHz. A linear increase in induced piezoelectricity to −3.0 C/m2 and −1.5 C/m2 at 110 kV/cm was observed in Ba0.6Sr0.4TiO3 on MgO and Ba0.7Sr0.3TiO3 on Si. Hysteresis in the piezoelectric and dielectric response of the 70:30 composition films was consistent with the positive irreversible dielectric Rayleigh coefficient. Both indicate a ferroelectric contribution to the piezoelectric and dielectric response over 40–80 °C above the global paraelectric transition temperature.
Document Details
- Document Type
- Pub Defense Publication
- Publication Date
- Sep 29, 2014
- Source ID
- 10.1063/1.4897299
Entities
People
- L. M. Garten
- S. Trolier-mckinstry
Organizations
- Pennsylvania State University