Effect of poling temperature on piezoelectric and dielectric properties of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 single crystals under alternating current poling
Abstract
In this work, the piezoelectric and dielectric properties of [001]-oriented 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 single crystals under alternating current poling (ACP) at different temperatures were studied. The piezoelectric coefficients (d33 ∼ 1930 pC/N, d31 ∼ −850 pC/N) and free dielectric permittivity (εT33/ε0 ∼ 7570) reached their highest values when the poling temperature (Tpoling) was 70 °C. Compared with traditional direct current electric field poling at 20 °C, 70 °C-ACP samples showed an enhancement of 40%, 35%, and 49% for d33, d31, and εT33/ε0, respectively. Meanwhile, d33 and εT33/ε0 were enhanced by about 9% when Tpoling increased from 20 °C to 70 °C under ACP, while d31 remained the same value and the dielectric loss was lowered from 0.29% to 0.22%. Moreover, ACP samples with different Tpoling have similar electromechanical coupling factors (k31 ∼ 0.44, kt ∼ 0.60). A discussion of the mechanism for the ACP enhancement was based on the domain observation using piezoresponse force microscopy, and the results showed that the domain densities of ACP samples with different Tpoling were positively correlated with their piezoelectric properties. This work demonstrated the enormous potential of ACP optimization for relaxor-PT single crystal applications.
Document Details
- Document Type
- Pub Defense Publication
- Publication Date
- Apr 29, 2019
- Source ID
- 10.1063/1.5094362
Entities
People
- Chengtao Luo
- Haotian Wan
- Wei-Yi Chang
- Xiaoning Jiang
- Yohachi Yamashita
Organizations
- National Science Foundation
- North Carolina State University
- Office of Naval Research