Indium as a surfactant: Effects on growth morphology and background impurity in GaN films grown by ammonia-assisted molecular beam epitaxy
Abstract
We report on the improvement of the surface morphology of c-plane GaN films grown at high growth rates (∼1 µm/h) using ammonia molecular beam epitaxy through a series of growth optimizations as well as the introduction of indium as a surfactant. The indium surfactant was expected to help with the adatom mobility and, thus, provide smoother growth surfaces. Through a combination of varying V/III ratios, In flux, and growth temperatures, an optimal condition for surface morphology, characterized by atomic force microscopy, was achieved. At higher Ga fluxes for fast growth rates (∼1 µm/h and beam equivalent pressures of ∼5 × 10−7 Torr), higher ammonia flows were necessary to preserve the surface morphology. In addition, indium was an effective surfactant—reducing the roughness and improving the overall surface morphology. However, excessive indium causes the surface morphology to degrade, potentially due to the enhancement of the Ga desorption from the surface as a result of the reaction of indium with ammonia for high indium fluxes. The indium surfactant also resulted in a reduction of background Si impurity concentrations in the film. These effects allow for the growth of thick drift layers with low background dopant concentrations for vertical GaN power devices.
Document Details
- Document Type
- Pub Defense Publication
- Publication Date
- Aug 01, 2022
- Source ID
- 10.1063/5.0098714
Entities
People
- Ashley Wissel
- Esmat Farzana
- James S. Speck
- Kai Shek Qwah
- Morteza Monavarian
- Tom Mates
Organizations
- ARPA-E
- Air Force Office of Scientific Research
- Simons Foundation
- University of California