Mechanical Characterization of Annealed ZrB2–SiC Composites
Abstract
Composites consisting of 70 vol% ZrB2 and 30 vol% α‐SiC particles were hot pressed to near full density and subsequently annealed at temperatures ranging from 1000°C to 2000°C. Strength, elastic modulus, and hardness were measured for as‐processed and annealed composites. Raman spectroscopy was employed to measure the thermal residual stresses within the silicon carbide (SiC) phase of the composites. Elastic modulus and hardness were unaffected by annealing conditions. Strength was not affected by annealing at 1400°C or above; however, strength increased for samples annealed below 1400°C. Annealing under uniaxial pressure was found to be more effective than annealing without applied pressure. The average strength of materials annealed at 1400°C or above was ~700 MPa, whereas that of materials annealed at 1000°C, under a 100 MPa applied pressure, averaged ~910 MPa. Raman stress measurements revealed that the distribution of stresses in the composites was altered for samples annealed below 1400°C resulting in increased strength.
Document Details
- Document Type
- Pub Defense Publication
- Publication Date
- Dec 06, 2012
- Source ID
- 10.1111/jace.12116
Entities
People
- Greg Hilmas
- Jeremy Watts
- William G. Fahrenholtz
Organizations
- Air Force Office of Scientific Research
- Missouri University of Science and Technology