Novel hard, tough HfAlSiN multilayers, defined by alternating Si bond structure, deposited using modulated high-flux, low-energy ion irradiation of the growing film
Abstract
Hf1−x−yAlxSiyN (0 ≤ x ≤ 0.14, 0 ≤ y ≤ 0.12) single layer and multilayer films are grown on Si(001) at 250 °C using ultrahigh vacuum magnetically unbalanced reactive magnetron sputtering from a single Hf0.6Al0.2Si0.2 target in mixed 5%-N2/Ar atmospheres at a total pressure of 20 mTorr (2.67 Pa). The composition and nanostructure of Hf1−x−yAlxSiyN films are controlled by varying the energy Ei of the ions incident at the film growth surface while maintaining the ion-to-metal flux ratio constant at eight. Switching Ei between 10 and 40 eV allows the growth of Hf0.78Al0.10Si0.12N/Hf0.78Al0.14Si0.08N multilayers with similar layer compositions, but in which the Si bonding state changes from predominantly Si–Si/Si–Hf for films grown with Ei = 10 eV, to primarily Si–N with Ei = 40 eV. Multilayer hardness values, which vary inversely with bilayer period Λ, range from 20 GPa with Λ = 20 nm to 27 GPa with Λ = 2 nm, while fracture toughness increases directly with Λ. Multilayers with Λ = 10 nm combine relatively high hardness, H ∼ 24 GPa, with good fracture toughness.
Document Details
- Document Type
- Pub Defense Publication
- Publication Date
- May 18, 2015
- Source ID
- 10.1116/1.4920980
Entities
People
- A. B. Mei
- Brandon M. Howe
- Grzegorz Greczynski
- Hanna Fager
- Ivan Petrov
- Jenny E. Greene
- Jens Jensen
- Jun Lü
- Lars Hultman
Organizations
- Air Force Research Laboratory
- Linköping University
- Swedish Foundation for Strategic Research
- Swedish Research Council
- United States Department of Defense
- United States Department of Energy
- University of Illinois Urbana–Champaign