Enhancing Fatigue Performance of Sandwich Composites with Nanophased Core
Abstract
We report fatigue performance of sandwich composites with nanophased core under shear load. Nanophased core was made from polyurethane foam dispersed with carbon nanofiber (CNF). CNFs were dispersed into part-A of liquid polyurethane through a sonication process and the loading of nanoparticles was 1.0 wt%. After dispersion, part-A was mixed with part-B, cast into a mold, and allowed to cure. Nanophased foam was then used to fabricate sandwich composites. Static shear tests revealed that strength and modulus of nanophased foams were 33% and 19% higher than those of unreinforced (neat) foams. Next, shear fatigue tests were conducted at a frequency of 3 Hz and stress ratio (R) of 0.1. S-N curves were generated and fatigue performances were compared. Number of cycles to failure for nanophased sandwich was significantly higher than that of the neat ones. For example, at 57% of ultimate shear strength, nanophased sandwich would survive 400,000 cycles more than its neat counterpart. SEM micrographs indicated stronger cell structures with nanophased foams. These stronger cells strengthened the sub-interface zones underneath the actual core-skin interface. High toughness of the sub-interface layer delayed initiation of fatigue cracks and thereby increased the fatigue life of nanophased sandwich composites.
Document Details
- Document Type
- Pub Defense Publication
- Publication Date
- Jan 01, 2010
- Source ID
- 10.1155/2010/712731
Entities
People
- H. Mahfuz
- S. Jeelani
- Shaik Zainuddin
Organizations
- Florida Atlantic University
- Office of Naval Research
- Tuskegee University