Characterization, Analysis and Significance of Defects in Composite Materials. Conference Proceedings: Meeting of the Structures and Materials Panel (56th) held in London, England on 12-14 April 1983
Abstract
Contents: Fractographic Analysis of Failures in CFRP; NDE Techniques for Composite Laminates; Monitoring of Defect Progression by Acoustic Emission; Growth of Delaminations Under Fatigue Loading; Experimental Investigation of Delaminations in Carbon Fibre Composite; Characterization of Cumulative Damage in Composites During Service; An Empirical Appraisal of Defects in Composites; Correlation Between Non-Destructive Inspection Results and Performance of Graphite/Epoxy Structural Parts; The Effect of Damage on The Tensile and Compressive Performance of Carbon Fibre Laminates; Behaviour of Idealized Discontinuities and Impact Damages In CFRP Under Fatigue Loading; Advanced N.D. Techniques for Composite Primary Structures; Computation of Influence of Defects on Static and Fatigue Strength of Composites; Fracture Mechanics of Sublaminate Cracks in Composite Laminates; The Significance of Defects and Damage in Composites Structures; In-Service NDI of Composite Structures: An Assessment of Current Requirements and Capabilities; Effect of Defects on Aircraft Composite Structures; The Engineering Significance of Defects in Composite Structures; Defect Occurrences in The Manufacture of Large CFC Structures and Work Associated with Defects, Damage and Repair of CFC Components; and Delamination Growth in Composite Structures Under InPlane Compression Loading.
Document Details
- Document Type
- Technical Report
- Publication Date
- Jul 01, 1983
- Accession Number
- ADA134058
Entities
People
- D. Purslow
- Franco Cipri
- George P. Sendeckyj
- Joachim Block
- M. Bourgeon
- M. E. Roylance
- Nigel Parslow
- R. Prinz
- W. Geier
Organizations
- AGARD