Controlling Fundamentals in High-Energy High-Rate Pulsed Power Materials Processing of Powdered Tungsten, Titanium Aluminides, and Copper-Graphite Composites
Abstract
This study was conducted to determine the controlling fundamentals in the high-energy high-rate (1 MJ in 1s) processing of metal powders. This processing utilizes a large electrical current pulse to heat a pressurized powder mass. The current pulse was provided by a homopolar generator. Simple short cylindrical shapes were consolidated so as to minimize tooling costs. Powders were subjected to current densities of 5 kA/cm2 to 25 kA/cm2 under applied pressures ranging from 70 MPa to 500 MPa. Disks with diameters of 25 mm to 70 mm, and thicknesses of 1 mm to 10 mm were consolidated. Densities of 75% to 99% of theoretical values were obtained in powder consolidates of tungsten, titanium aluminides, copper-graphite, and other metal-ceramic composites. Extensive microstructural characterization was performed to follow the changes occuring in the shape and microstructure of the various powders. The processing science has at its foundation the control of the duration of elevated temperature exposure during powder consolidation.
Document Details
- Document Type
- Technical Report
- Publication Date
- Oct 01, 1990
- Accession Number
- ADA230900
Entities
People
- C. Persad
- D. L. Bourell
- Harris L. Marcus
- William F. Weldon
- Z. Eliezer
Organizations
- University of Texas at Austin