Fabrication and Investigation of Intermetallic Compound-Glassy Phase Composites having Tensile Ductility
Abstract
The purpose of this research was to produce in-situ ductile crystalline intermetallic compound-glassy composite materials with high strength and good plasticity. A range of composite specimens was prepared (Cu-Y, Y-Cu-Ag, Y-Cu-Al, Cu-Y-Ag, Mg-Cu-Y, Mg-Y-Ag, Mg-Y-Zn, Ni-Cu-Ti-Zr) using casting and melt spinning techniques. Structure was examined by x-ray diffraction; phase transformations were studied by differential scanning and isothermal calorimetry. Crystal-glassy composites formed in Y-Cu-Ag, Y-Cu-Al and Cu-Y-Ag and Ni-Cu-Ti-Zr alloys whereas Mg-based alloys did not smelt well. Ribbon samples of Y-Cu-Ag, Y-Cu-Al and Cu-Y-Ag alloys showed good bending ductility while bulk Ni-Cu-Ti-Zr alloy samples of 2 mm in diameter demonstrated large plasticity owing to martensitic transformation in B2 crystalline phase and TRIP effect. Large deformations up to about 20% were achieved in Ni-Cu-Ti-Zr alloys.
Document Details
- Document Type
- Technical Report
- Publication Date
- Aug 09, 2012
- Accession Number
- ADA564806
Entities
People
- Dmitri Louzguine
Organizations
- Tohoku University