Initial Assessment of the Effects of Nonmetallic Inclusions on Fatigue Life of Powder-Metallurgy-Processed Udimet(R) 720
Abstract
The fatigue lives of modern powder metallurgy (PM) disk alloys are influenced by variabilities in alloy microstructure and mechanical properties. These properties can vary due to the different steps of materials/component processing and machining. One of these variables, the presence of nonmetallic inclusions. has been shown to significantly degrade low-cycle fatigue (LCF) life. Nonmetallic inclusions are inherent defects in powder alloys that are a by-product of powder-processing techniques. Contamination of the powder can occur in the melt, daring powder atomization. or during any of the various handling processes through consolidation. In modem nickel disk powder processing facilities. the levels of inclusion contamination have been reduced to less than 1 part per million by weight. Despite the efforts of manufacturers to ensure the cleanliness of their powder production processes, the presence of inclusions remains a source of great concern for the designer. The objective of this study was to investigate the effects on fatigue life of these inclusions. Since natural inclusions occur so infrequently, elevated levels of inclusions were carefully introduced in a nickel-based disk superalloy, Udimet(registered) 720 (registered trademark of Special Metals Corporation), produced using PM processing. Multiple strain- controlled fatigue tests were then performed on this material at 650 deg C. Analyses were performed to compare the LCF lives and failure initiation sites as functions of inclusion content and fatigue conditions. A large majority of the failures in specimens with introduced inclusions occurred at cracks initiating from inclusions at the specimen surface. The inclusions could reduce fatigue life by up to 1003. These effects were found to be dependent on strain range and strain ratio. Tests at lower strain ranges and higher strain ratios produced larger effects of inclusions on life.
Document Details
- Document Type
- Technical Report
- Publication Date
- Aug 01, 2002
- Accession Number
- ADA406107
Entities
People
- J. Telesman
- P. J. Bonacuse
- P. T. Kantzos
- R. L. Barrie
- T. P. Gabb
Organizations
- National Aeronautics and Space Administration